牌号简介 About |
---|
它是热塑性弹性体(TPE)系列中的一种可着色的特种热塑性硫化弹性体(TPV)。 它专为与 PC、ABS、PC/ABS 和 PMMA 粘结而配制,适用于要求硬/软材料组合的应 用。这一牌号的山都平 TPV 是剪切速率依赖型产品,可在常规热塑性注塑成型或 挤出成型设备上加工。可在线回收利用。 A colorable, specialty thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It is especially formulated to bond to PC, ABS, PC/ABS, ASA and PMMA for applications where hard/soft combinations are required. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It is recyclable within the manufacturing stream. |
产品描述 Product Description
厂家:美国塞拉尼斯 Celanese
类别:TPV
用途:粘结树脂;疲劳消除用品;体育用品;消费品应用领域;电器用具;粘合;家电部件;手机;柔软的把手;汽车领域的应用;镜架;活动的铰链;密封件;大型家用电器和小型家用电器;厨具;汽车的发动机罩下的零件;
颜色:自然色
加工条件:注射成型,多次注射成型,共挤出成型 Injection Molding,Multiple injection molding
性能特点: 可回收; 防火阻燃等级HB; 耐油; 耐化学性; 减震; 耐臭氧; 可粘结性; noise reduction,HB,Renewable resources,Agglomerability,Solvent resistance,Ozone resistance,Grease resistance
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.10 | g/cm³ | ASTM D792 |
密度 Density |
1.10 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
15.4 | MPa | ASTM D412 |
TD,断裂,23℃ TD, fracture, 23 ℃ |
15.4 | MPa | ISO 37 |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
3.20 | MPa | ISO 37 |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ISO 37 | |
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ASTM D412 | |
撕裂强度 tear strength |
|||
TD,23℃ TD,23℃ |
kN/m | ASTM D624 | |
TD,23℃ TD,23℃ |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
ASTM D395B | ||
23℃,22 hr 23℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
压缩形变 Compression deformation |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,15 秒,23℃ Shore A, 15 seconds, 23 ℃ |
ISO 868 | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度的变化率 在空气中(100℃,168 hr) The rate of change in tensile strength in air (100 ℃, 168 hr) |
% | ASTM D573 | |
拉伸强度的变化率 在空气中(100℃,168 hr) The rate of change in tensile strength in air (100 ℃, 168 hr) |
% | ISO 188 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
Change in Tensile Strain at Break in Air(100℃,168 hr) Change in Tensile Strain at Break in Air(100℃,168 hr) |
% | ISO 188 | |
拉伸强度的变化率 The rate of change in tensile strength |
ASTM D471 | ||
23℃,24 hr,in IRM 903 Oil 23℃,24 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
% | ASTM D471 | |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
% | ASTM D471 | |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,在相对湿度,90% 23 ℃, 168 hr, at relative humidity of 90% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
38℃,168 hr,在相对湿度,90% 38 ℃, 168 hr, at relative humidity of 90% |
% | ASTM D471 | |
拉伸强度的变化率 The rate of change in tensile strength |
ISO 1817 | ||
23℃,24 hr,in IRM 903 Oil 23℃,24 hr,in IRM 903 Oil |
% | ISO 1817 | |
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
% | ISO 1817 | |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
% | ISO 1817 | |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
% | ISO 1817 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23℃,168 hr,在相对湿度,90% 23 ℃, 168 hr, at relative humidity of 90% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
38℃,168 hr,在相对湿度,90% 38 ℃, 168 hr, at relative humidity of 90% |
% | ISO 1817 | |
极限伸长率的变化率 Change rate of ultimate elongation |
ASTM D471 | ||
23℃,24 hr,in IRM 903 Oil 23℃,24 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
% | ASTM D471 | |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
% | ASTM D471 | |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,在相对湿度,90% 23 ℃, 168 hr, at relative humidity of 90% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
38℃,168 hr,在相对湿度,90% 38 ℃, 168 hr, at relative humidity of 90% |
% | ASTM D471 | |
断裂时拉伸应力变化 Changes in tensile stress during fracture |
ISO 1817 | ||
23℃,24 hr,in IRM 903 Oil 23℃,24 hr,in IRM 903 Oil |
% | ISO 1817 | |
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
% | ISO 1817 | |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
% | ISO 1817 | |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
% | ISO 1817 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23℃,168 hr,在相对湿度,90% 23 ℃, 168 hr, at relative humidity of 90% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
38℃,168 hr,在相对湿度,90% 38 ℃, 168 hr, at relative humidity of 90% |
% | ISO 1817 | |
Change in Durometer Hardness(邵氏 A,23℃,168 hr,in Deionized Water) Change in Durometer Hardness (23 ℃, 168 hr, in Deionized Water) |
ASTM D471 | ||
邵氏硬度的变化率 The rate of change in Shore hardness |
|||
邵氏 A,23℃,168 hr,在去离子水中 Shore A, 23 ℃, 168 hr, in deionized water |
ISO 1817 | ||
质量变化率 Quality change rate |
ASTM D471 | ||
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
% | ASTM D471 | |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
% | ASTM D471 | |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,在相对湿度,95% 23 ℃, 168 hr, at relative humidity of 95% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
38℃,168 hr,在相对湿度,95% 38 ℃, 168 hr, at relative humidity of 95% |
% | ASTM D471 | |
质量变化率 Quality change rate |
ISO 1817 | ||
23.0℃,168 hr,在相对湿度,95% 23.0 ℃, 168 hours, at relative humidity of 95% |
% | ISO 1817 | |
23.0℃,168 hr,in Sodium Hydroxide,50% 23.0℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
30.0℃,168 hr,在相对湿度,95% 30.0 ℃, 168 hours, at relative humidity of 95% |
% | ISO 1817 | |
23.0℃,168 hr,in Cascade Detergent 23.0℃,168 hr,in Cascade Detergent |
% | ISO 1817 | |
23.0℃,168 hr,in Sodium Chloride,15% 23.0℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23.0℃,168 hr,in Hydrochloric Acid,10% 23.0℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23.0℃,168 hr,in Clorox,10% 23.0℃,168 hr,in Clorox,10% |
% | ISO 1817 | |
23.0℃,168 hr,in Ethanol,50% 23.0℃,168 hr,in Ethanol,50% |
% | ISO 1817 | |
体积变化 Volume change |
ASTM D471 | ||
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
% | ASTM D471 | |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
% | ASTM D471 | |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
% | ASTM D471 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ASTM D471 | |
23℃,168 hr,在相对湿度,95% 23 ℃, 168 hr, at relative humidity of 95% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
38℃,168 hr,在相对湿度,95% 38 ℃, 168 hr, at relative humidity of 95% |
% | ASTM D471 | |
体积变化 Volume change |
ISO 1817 | ||
23℃,168 hr,in Cascade Detergent 23℃,168 hr,in Cascade Detergent |
% | ISO 1817 | |
23℃,168 hr,in Clorox,10% 23℃,168 hr,in Clorox,10% |
% | ISO 1817 | |
23℃,168 hr,in Ethanol,50% 23℃,168 hr,in Ethanol,50% |
% | ISO 1817 | |
23℃,168 hr,in Hydrochloric Acid,10% 23℃,168 hr,in Hydrochloric Acid,10% |
% | ISO 1817 | |
23℃,168 hr,在相对湿度,95% 23 ℃, 168 hr, at relative humidity of 95% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
38℃,168 hr,在相对湿度,95% 38 ℃, 168 hr, at relative humidity of 95% |
% | ISO 1817 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
2.10 mm 2.10 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 B 方法,直角形试样(割口) |
4 类型 1 |
5 类型 A |
【新闻资讯】查看全部
【生活中的LG化学】耐前照灯的光线
2020-09-20 搜料网资讯: 选择汽车时,设计是非常重要的基准。 虽然决定设计的因素有很多,但是前照灯在决定汽车第一印象方面发挥着重大作用。 这是因为被称为汽车之眼的前照灯位于汽车前 |
【生活中的LG化学】耐前照灯的光线 搜料网资讯:选择汽车时,设计是非常重要的基准。虽然决定设计的因素有很多,但是前照灯在决定汽车第一印象方面发挥着重大作用。 这是因为被称为汽车之眼的前照灯位于汽车前部,体现了汽车固有的风格。独特的前照灯设计还可以代表特定车辆的形象。此外,前照灯在功能上也起到了非常重要的作用。 黑暗时发光以确保汽车的视野,并告知其它车辆和行人该车辆的存在。 前照灯由多个配件组成,灯圈是灯的边框部分,起到分配灯内部光线的作用。用于该灯圈的原材料需要可以承受灯放射出的较高热量,并且要求具有高冲击强度、高光泽等优越性能。 所以使用高功能性的工程塑料而不是普通塑料,其中常用的是以 PBT(Polybutyleneterephthalate,聚对苯二甲酸丁二酯)为基材,与其它原材料合铸而成的材料。 LG化学中以 LUPOX 为名进行生产。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 汽车密封件
- 2019-06-26 0
- Santoprene™ 291-60B150是热塑性弹性体(TPE)系列中的一种可着色的特种热塑性硫化弹性体(TPV)。 它专为与 PC、ABS、PC/ABS 和 PMMA 粘结而配制,适用于要求硬/软材料组合的应 用。
- 阅读全文
汽车密封件
收起
- 汽车换挡杆防尘罩
- 2019-06-26 0
- Santoprene™ 291-75B150是热塑性弹性体(TPE)系列中的一种可着色的特种热塑性硫化弹性体(TPV)。 它专为与 PC、ABS、PC/ABS 和 PMMA 粘结而配制,适用于要求硬/软材料组合的应 用。
- 阅读全文
汽车换挡杆防尘罩
1-Santoprene™ 291-75B150是热塑性弹性体(TPE)系列中的一种可着色的特种热塑性硫化弹性体(TPV)
2-拉伸强度(TD,100% 应变,23℃) 3.20 MPa
3-拉伸应变(TD,断裂,23℃) 640 %
4-压缩形变(23℃,22 hrs) 37 %
5-邵氏硬度(邵氏 A,15 秒,23℃) 74
2-拉伸强度(TD,100% 应变,23℃) 3.20 MPa
3-拉伸应变(TD,断裂,23℃) 640 %
4-压缩形变(23℃,22 hrs) 37 %
5-邵氏硬度(邵氏 A,15 秒,23℃) 74
收起
抱歉!暂无数据。