牌号简介 About |
---|
PBT+PC,UL94V-0/5VA额定,冲击修改,不透明,未加固。诸如线轴、开关和外壳等应用。 PBT+PC, UL94V-0/5VA Rated, Impact Modified, Opaque, Unreinforced. Applications like bobbins, switches and enclosures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.35 | g/cm³ | ASTM D792 |
特定体积 Specific volume |
0.740 | cm³/g | ASTM D792 |
密度 Density |
1.34 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,5.0kg 250℃,5.0kg |
9.6 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
250℃,5 kg 250℃,5 kg |
8.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
Internal Method | ||
TD TD 2 |
% | 内部方法 | |
TD TD 3 |
% | 内部方法 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
24hr 24hr |
% | ASTM D570 | |
耐候性 Weathering resistance |
UL 746C | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 9 |
|||
23℃ 23℃ 9 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 10 |
ISO 180/1A | ||
23℃ 23℃ |
ASTM D4812 | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
落锤冲击 Drop hammer impact |
ASTM D3029 | ||
23℃ 23℃ |
J | ASTM D3029 | |
23℃ 23℃ 11 |
J | ASTM D3029 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 12 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 13 | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test 14 |
|||
125℃ 125℃ 14 |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD MD |
ASTM E831 | ||
-40 到 40℃ -40 to 40 ℃ |
cm/cm/℃ | ASTM E831 | |
60 到 138℃ 60 to 138 ℃ |
cm/cm/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
ASTM D149 | ||
1.6 mm,在油中 1.6 mm in oil |
kV/mm | ASTM D149 | |
3.2 mm,在空气中 3.2 mm in air |
kV/mm | ASTM D149 | |
3.2 mm,在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance 15 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.46 mm 0.46 mm |
UL 94 | ||
0.63 mm 0.63 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0 mm 1.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
2 mm 2 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 4 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength 6 |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 5 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
屈服 yield 6 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 5 |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 5 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 5 |
% | ASTM D638 | |
弯曲模量 Bending modulus 7 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 7 |
MPa | ASTM D790 | |
弯曲强度 bending strength 7 , 8 |
MPa | ISO 178 | |
弯曲强度 bending strength 7 |
|||
断裂,50 mm跨度 Fracture, 50 mm span 6 |
MPa | ASTM D790 | |
屈服,50 mm跨度 Yield, 50 mm span 7 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
特殊值 Special value |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
MD MD 2 |
% | 内部方法 | |
MD MD 3 |
% | 内部方法 | |
MD:3.2 mm MD:3.2 mm |
% | 内部方法 | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.75 to 2.3 mm |
3 2.3 to 4.6 mm |
4 0.20 in/min |
5 类型 1, 2.0 in/min |
6 0.051 in/min |
7 0.079 in/min |
8 Yield |
9 80*10*4 sp=62mm |
10 80*10*4 |
11 Modified |
12 80*10*4 mm |
13 标准 B (120°C/h), 载荷2 (50N) |
14 by VDE |
15 钨电极 |
【新闻资讯】查看全部
国际首家注拉吹模内贴标产品展现会圆满举行
2016-01-11 随着中国人口红利的优势不复存在以及就业观的波动性,企业必须进行产业结构升级,满足全自动化生产。在这种大背景下,佛山市顺德区工正包装设备制造有限公司于1月8日隆重举办“国内首家注拉吹模内贴标产品展示会”。优泊公司代表、广州市新汕纸业有限公司代表、广州新标机电科技有限公司代表、深圳坤邦标价用品有限公司代表等超过百余名嘉宾应邀参加了本次展示会。 下午1时,“国内首家注拉吹模内贴标产品展示会”在热烈的掌声中拉开帷幕。随后,到场嘉宾在工正包装设备制造有限公司陈艺力总经理的带领下进入生 |
国际首家注拉吹模内贴标产品展现会圆满举行 伴随着我国人口老龄化的优点荡然无存及其择业观的不确定性,公司务必开展产业布局升級,考虑全自动化生产。在这类大情况下,东莞市佛山顺德工正包装机械设备生产制造有限责任公司于1月8日庄重举行“中国第一家注拉吹模内贴标产品展销会”。优泊企业代表、广州新汕纸制品厂有限责任公司代表、广州市国家免检产品机电工程高新科技有限责任公司代表、深圳市坤邦定价用具有限责任公司代表等超出数百名嘉宾应邀参加了此次展销会。 中午1时,“中国第一家注拉吹模内贴标产品展销会”在掌声雷动中拉开序幕。接着,在场嘉宾在工正包装机械设备生产制造有限责任公司陈艺力经理的领着下进到生产线参观考察。在工正企业整洁齐整的生产厂家房内,在场嘉宾一起收看了注拉吹模内技术性演试。 当场嘉宾参观考察注拉吹模内技术性演试 在注拉吹模内技术性演试当场,陈总表明,做为致力于公司精密度及品质规定高的空心产品出示降低成本、节能型的解决方法的顶级公司,东莞市佛山顺德工正包装机械设备生产制造有限责任公司开创于2000年,企业产品研发的GZ-SS400-TI型注拉吹三工序空心成形机器设备、GZ-SS400-FI型注拉吹四工序空心成形机器设备、一步法成形机器设备模貝为饮品、PP输液器、PET药品包装设计、高端护肤品等行业公司出示高效率环保节能的解决方法。在其中一步法机器设备也是喜获国家发明专利,为公司处理产业布局升級,人口老龄化没有等急迫难题出示极致解决方法。 中午3时,参会嘉宾启航前去长鹿农庄开展会议报告。在大会当场,陈总干了“中国第一家注拉吹模内贴标成效新品发布会”主题风格演说。他表明,伴随着中国市场经济体制的发展趋势,尤其是食品类、日化用品、药业、电子器件产品及其商场、货运物流等领域的迅速发展趋势,使我国标识产业链展现飞越式发展趋势,年产值及总产量均完成髙速提高。2012年不干胶印刷工业产值完成260亿人民币,生产量完成34亿平方米,较2011年各自提高13%和14%。在我国标识业髙速发展趋势的另外,一些具有发展潜力的新式标识技术性逐渐慢慢出类拔萃,模内贴标签便是在其中之一。 东莞市佛山顺德工正包装机械设备生产制造有限责任公司经理陈艺力老先生做“中国第一家注拉吹模内贴标成效新品发布会”主题风格演说 中国第一家注拉吹模内贴标成效新品发布会当场 近几年来,酸牛奶、奶酪等乳业领域的高效益产品也在趋于运用模内贴标包装设计。针对模内贴标包装设计的主要表现,光明乳业一位包裝责任人详细介绍说:“现阶段模内贴标包装设计关键运用在光明乳业1911系列产品原酪酸牛乳、属实系列产品酸牛奶和乳酪三大产品中。从实际效果看来,产品包裝品质十分平稳。会挑选模内贴标包装设计,关键来源于现如今顾客对包裝规定很高,包裝在一定水平上决策了产品的级别印像,危害产品营销推广实际效果,而模内贴标包装设计相较别的包裝方式,很切实解决了标识易掉、翘边的难题,包裝更美观大方,能够大大的提高产品的竞争能力。“模内贴标技术性简单化了吹瓶生产工艺流程,一站式生产制造出“穿着打扮”的产品,提升了产品加工工艺综合性使用价值,对吹瓶厂来讲既提高产品竞争能力,又提升产品增加值。”陈总最终汇总道。 在接着开展的当场互动交流沟通交流与话题讨论阶段,参会嘉宾竞相就当今中国市场走势及其对注拉吹模内贴标产品的行业前景开展了热情的探讨。一部分公司也传道授业,共享她们对注拉吹模内贴标产品的观点及其在注拉吹模内技术性层面的工作经验,得到当场嘉宾的一阵阵欢呼声。当场观众们也就一些难题明确提出自身的疑虑,嘉宾们也不遗余力得出自身的见解,让大会再上一个高潮迭起。 PET模内贴标加工工艺 模内贴标制成品 来源于:慧聪胶网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
- 线轴
- 2019-11-05 0
- VALOX™ 357 resin为PBT+PC混合物,UL94V-0/5VA额定,冲击修改,不透明,未加固。诸如线轴、开关和外壳等应用。
- 阅读全文
线轴
抱歉!暂无数据。